Oxime type curing, one component,strong mechanical performance after curing. SV709 has fast skin forming time,and easy to use.SV709 has successful application case on solar industy, itwill skin formed in a few minutes and cahieved enough mechanical property to meet the requirement of the solar production line.After cured, SV709 will provide long term protection to solar power.
Products | JS-606 | JS-606CHUN | Test Methods |
color | White/black | White/black | Visual |
g/cm3 Density | 1.41±0.05 | 1.50±0.05 | GB/T 13477-2002 |
Solidification type | oxime | /alkoxy | / |
Tack-Free Time, min | 5~20 | 3~15 | GB/T 13477 |
Durometer hardness, Shore A | 40~60 | 40~60 | GB/T 531-2008 |
Tensile strength, MPa | ≥2.0 | ≥1.8 | GB/T 528-2009 |
Elongation at Break, % | ≥300 | ≥200 | GB/T 528-2009 |
Volume resisitivity, Ω.cm | 1×1015 | 1×1015 | GB/T1692 |
disruptive strength,KV/mm | ≥17 | ≥17 | GB/T 1695 |
W/m.k Thermal conductivity | ≥0.4 | ≥0.4 | ISO 22007-2 |
Fire resistance,UL94 | HB | HB | UL94 |
ºC Working temperature | -40~200 | -40~200 | / |