| Material: | Organic Silicone |
|---|---|
| Application: | Household, Medical, Industrial, Agricultural |
| Certification: | ISO, FDA, REACH |
| Color: | Clear\Black\White\Gray\Others Silicone Sealant |
| Sample: | Free Sample Stone Silicone Sealant |
| Keyword: | Medium Modulus |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier 
SikaHyflex®-305 AP is a 1-component, moisture curing, low-modulus elastic weather sealant.
600 ml foil pack, 20 foil packs per box
Black, Grey (MTO)
Use closed cell, polyethylene foam backing rods.
|
~ 2 mm (20 mm profile, 50 °C) |
(ISO 7390) |
+5 °C to +40 °C, min. 3 °C above dew point temperature
+5 °C to +40 °C
|
~ 2 mm/24 hours (23 °C / 50% r.h.) |
(CQP 049-2) |
|
~ 25 minutes (23 °C / 50% r.h.) |
(CQP 019-1) |
|
~ 160 minutes (23 °C / 50% r.h.) |
(CQP 019-1) |
Sikaflex®-252 is an elastic 1-component polyurethane adhesive especially designed for bonding large components in vehicle assembly. It is suitable for bonding coated metal, GRP, ceramic materials and plastics.
|
Cartridge |
300 ml |
| Unipack | 600 ml |
| Chemical base |
1-component polyurethane
|
|
| Colour (CQP001-1) |
Black, white
|
|
| Cure mechanism |
Moisture-curing |
|
| Density (uncured) |
depending on colour
|
1.2 kg/l
|
| Non-sag properties |
Good |
|
| Application temperature |
ambient |
10 ─ 35 °C |
| Skin time (CQP019-1) |
40 minutes A |
|
| Open time (CQP526-1) |
35 minutes A
|
|
| Curing speed (CQP049-1) |
(see diagram 1)
|
|
| Shore A hardness (CQP023-1 / ISO 48-4) |
50 |
|
| Tensile strength (CQP036-1 / ISO 527) |
3 MPa |
|
| Elongation at break (CQP036-1 / ISO 527) |
400 % |
|
| Tear propagation resistance (CQP045-1 / ISO 34) |
7 N/mm
|
|
| Tensile lap-shear strength (CQP046-1 / ISO 4587) |
2.5 MPa |
|
| Service temperature (CQP509-1 / CQP513-1) |
4 hour 1 hour
|
-40 ─ 90 °C 130 °C 150 °C
|
| Shelf life (CQP016-1) |
12 months B
|
|
CQP = Corporate Quality Procedure |
A) 23 °C / 50 % r. h. |
B) storage below 25 °C |
Surfaces must be clean, dry and free from grease, oil, dust and contaminants.
The surface treatment depends on the specific nature of the substrates and is crucial for a long lasting bond. Suggestions for surface preparation may be found in the current edition of the appropriate Sika® Pre-treatment Chart. Consider that these suggestions are based on experience and must be verified by tests on original substrates.
Application
Sikaflex®-252 can be processed between 10 °C and 35 °C (climate and product) but changes in reactivity and application properties have to be considered. The optimum temperature for substrate and sealant is between 15 °C and 25 °C.
Consider that the viscosity will increase at low temperature. For easy application, condition the adhesive at ambient temperature prior to use. To ensure a uniform thickness of the bondline it is recommend to apply the adhesive in form of a triangular bead.
Sikaflex®-252 can be processed with manual, pneumatic or electric driven piston guns as well as pump equipment. The open time is significantly shorter in hot and humid climates. The parts must always be installed within the open time. Never join bonding parts if the adhesive has built a skin.
Tooling and finishing must be carried out within the skin time of the product. It is recommended to use Sika® Tooling Agent N. Other finishing agents must be tested for suitability and compatibility prior to use.
Uncured Sikaflex®-252 can be removed from tools and equipment with Sika® Remover-208 or another suitable solvent. Once cured, the material can only be removed mechanically. Hands and exposed skin have to be washed immediately using hand wipes such as Sika® Cleaner-350H or a suitable industrial hand cleaner and water.
Do not use solvents on skin.